摘要
Based on the theory of grain boundary segregation, a kinetics model of temper em-brittlement caused by long-term service for hot-wall hydrofining reactors was studied.The kinetics model was applied to phosphorus (P) segregation in 2.25Cr-1Mo steelused for a hot-wall hydrofining reactor, and the kinetics of grain boundary segrea-tion of impurity P in the steel exposed to the process environment of the hydrofiningreactor was calculated on the basis of the model. The Auger electron spectroscopytest was performed in order to determine the grain boundary concentration of P. Theexperimental result is agreement with the theoretical calculated data. The results showthat the kinetics equation is reasonable for predicting the levels of grain boundarysegregation of impurity P in 2.25Cr-1Mo steel used for hot-wall hydrofining reactors.
Based on the theory of grain boundary segregation, a kinetics model of temper em-brittlement caused by long-term service for hot-wall hydrofining reactors was studied.The kinetics model was applied to phosphorus (P) segregation in 2.25Cr-1Mo steelused for a hot-wall hydrofining reactor, and the kinetics of grain boundary segrea-tion of impurity P in the steel exposed to the process environment of the hydrofiningreactor was calculated on the basis of the model. The Auger electron spectroscopytest was performed in order to determine the grain boundary concentration of P. Theexperimental result is agreement with the theoretical calculated data. The results showthat the kinetics equation is reasonable for predicting the levels of grain boundarysegregation of impurity P in 2.25Cr-1Mo steel used for hot-wall hydrofining reactors.