The nanocrystals Er_2O_3 were prepared by using a combustion method with Schiff base as a chelating agent. The Er(Ⅲ) coordanation compound of Schiff base, obtained from erbium nitrate and retinal Schiff base, underwent a combustion process and voluminous ashes formed when calcimining the complex in air. Pure cubic Er_2O_3 nanocrystals with a diameter of 13 nm were produced. The nanocrystals were homogeneous and rigid coacervation was not observed. The photoluminescence emission spectrum of the erbium(Ⅲ) oxide nanocrystals shows that it has a characteristic peak at 1 54 μm, and some other shoulder peaks appear on both sides of the main peak.
The nanocrystals Er_2O_3 were prepared by using a combustion method with Schiff base as a chelating agent. The Er(Ⅲ) coordanation compound of Schiff base, obtained from erbium nitrate and retinal Schiff base, underwent a combustion process and voluminous ashes formed when calcimining the complex in air. Pure cubic Er_2O_3 nanocrystals with a diameter of 13 nm were produced. The nanocrystals were homogeneous and rigid coacervation was not observed. The photoluminescence emission spectrum of the erbium(Ⅲ) oxide nanocrystals shows that it has a characteristic peak at 1 54 μm, and some other shoulder peaks appear on both sides of the main peak.
基金
ProjectsupportedbytheNationalDefenseScienceFoundation (99J12 .2 .1HK)