在“球－盘”试验机上对Ｎｉ／ＭｏＳ２与 Ｎｉ－Ｐ／ＭｏＳ２两种复合镀层的摩擦磨损性能进行全面的测试与比较，并对其作用机理进行了分析。试验结果表明，两种复合镀层在油润滑条件下的摩擦系数，一般均可达到 ０．０５～０．０６的水平，而 Ｎｉ－Ｐ／ＭｏＳ２的承载能力或磨损寿命要比 Ｎｉ／ＭｏＳ２提高 ４～６倍以上。
Investigation and comparison of two composite plating layers on a 'ball-on-disc' testing machine under lubrication were conducted to evaluate their friction-reducing property, and the mechanism of their tribological behaviors were comprehensively analysed, The results showed that the friction coefficients of both composite plating layers can reach generally 0.05-0.06, and the wear-resistance of Ni-P/MoS2 is 4-6 times that of Ni/MoS2.