摘要
通过调整软质熔剂和硬质熔剂的种类和数量 ,研制出了适合刚玉质强化瓷的釉面硬度 7373MPa、白度 75 .9%、光泽度 89.
By adjusting several kinds and the relationship of the hard and soft fluxes,a high thermal shock resistance being adapted for high alumina strengthen porcelain product has been obtained.The flexural strength and hardness of the product are 140MPa and 7373MPa respectively.