摘要
The results of the study of the effect of partial substitution of Fe by Mn in the La Fe_(11.2-x)Mn_(x)Co_(0.7)Si_(1.1)system on magnetization,specific heat,magnetostriction and magnetocaloric effect are presented.Direct measurements of the adiabatic temperature change(ΔT_(ad))were carried out in alternating magnetic fields(AMF)using the magnetic field modulation method.Partial substitution of Fe atoms by Mn atoms leads to a shift in the Curie temperature(T_(C))towards lower temperatures without a noticeable deterioration in magnetic properties.A correlation was found between the structural component of the magnetocaloric effect and the stability of the frequency of theΔT_(ad)in the AMFs—an increase in the manganese concentration leads to a decrease in magnetostriction and to a lower dependence ofΔT_(ad)on the frequency of the magnetic field.Estimates of the specific cooling power Q_(C)as a function of the frequency of the AMF showed that the highest value of Q_(C)at f=20 Hz in a magnetic field of 12k Oe is 26.3 W g^(-1)and is observed for the composition with x=0.1.This value is higher than that of Gd,for which,under the same conditions,Q_(C)=21.6 W g^(-1).All the samples studied show stability of the value ofΔT_(ad)without any sign of deterioration of the effect up to 60,000cycles of switching on/off of the magnetic field of 12 k Oe.The discovered frequency and cyclic stability ofΔT_(ad)of the studied samples increase their prospects for application in magnetic cooling technology.
基金
financially supported by Russian Science Foundation(No.24-43-00156,https://rscf.ru/en/project/24-43-00156/)
the National Natural Science Foundation of China(No.52171169)
the State Key Laboratory for Advanced Metals and Materials(No.2023-ZD01)。