The Mg-9Li-1Zn(LZ91)alloy was subjected to an ultrasonic surface rolling process(USRP)with varying passes for the purpose of modifying its surface state.The USRP transformed surface residual stress from initial tensile stress to compressive stress,decreasing the surface roughness and increasing the ratio of the β-Li phase.The USRPed LZ91 sample(3 passes)showed superior corrosion resistance,with the corrosion current density changing from 57.11 to 24.70μA cm^(-2),and the polarization resistance increasing from 576.3 to 1146.1Ωcm^(2).According to the corrosion procedure evaluations,in situ observation revealed that the LZ91 alloy initially experiences pitting,which subsequently develops into cracking.The substantial area coverage of the β-Li phase facilitates the formation of a protective film on the surface,effectively delaying localized corrosion.
基金
financially supported by the National Natural Science Foundation of China(No.52271091)
the National Key Research and Development Program of China(No.2021YFB3701100)
the Natural Science Foundation Project of Ningxia Province(No.2023AAC03324).