摘要
High-efficiency formamidinium lead iodide(FAPbI3)-based perovskite solar cells(PSCs)typically involve annealing in humid air during the fabrication process of perovskite films.However,the combined effects of humidity and relatively high temperature often result in the uncontrollable formation of a detrimental PbI_(2)phase in the perovskite films.As a result,the annealing process of perovskite films is highly sensitive to the relative humidity fluctuations of the environment.Under solar illumination,the undesired PbI_(2)tends to decompose,accelerating the degradation of perovskite materials and severely compromising the light stability of PSCs.This issue is particularly critical for the buried interface and bulk of the perovskite films,as these regions absorb the majority of the incident light.Pre-treatment and posttreatment strategies are generally confined to address the PbI_(2)issues at the buried interface and on the surface of the perovskite films,respectively.However,effectively addressing the effects of excess PbI_(2)at buried interface and grain boundaries within bulk in a single step remains challenging.In this study,we propose an intermediate-treatment strategy using phthalylglycyl chloride(PTC),which involves treating the wet films with PTC prior to annealing during the formation process of the perovskite films.This approach protects the grain boundaries of polycrystalline perovskite films in advance,effectively preventing moisture-induced degradation of the perovskites and thus significantly broadening the relative humidity window of annealing process.Our results demonstrate that this strategy can successfully suppress the formation of PbI_(2)at the grain boundaries and buried interface of perovskite films,thereby eliminating the PbI_(2)-induced degradation pathways.Our strategy significantly reduces the sensitivity to humidity fluctuations during annealing for fabricating stable PSCs,ensuring more consistent fabrication of stable PSCs.Consequently,the resulting PSCs achieve a champion power conversion efficiency of 26.1% and demonstrate excellent light stability.
基金
financially supported by the National Natural Science Foundation of China(52203208,52325310,U24A6003,52303335)
the National Key R&D Program of China(2021YFB3800101)
the Beijing Nova Program(contract no.20230484480)
the open research fund of Songshan Lake Materials Laboratory(2022SLABFK07)
the Yunnan Provincial Science and Technology Project at Southwest United Graduate School(202302AO370013)
the R&D Fruit Fund(20210001)。