摘要
气凝胶作为最有潜力的绝热材料,被广泛应用于航空航天、军工、建筑保温等领域。然而传统气凝胶因疏水基团的限制仅可在650℃以内适用,严重制约着其在高温窑炉等领域的推广应用。基于此,选取氧氯化锆为前驱体,以溶胶-凝胶工艺探究干燥工艺对耐高温锆(Zr)基及锆/硅复合基气凝胶材料的影响,并对其耐高温特性进行论证。结果表明,Zr基、Zr/Si基复合材料均表现出高比表面积,低导热系数,耐高温环境等性能特征,在水泥窑及耐火材料改性等新材料方向具有一定的应用潜力。
Aerogel,a promising porous material with ultra-low thermal conductivity,is widely used in aerospace,military,and building insu-lation.However,traditional aerogels are restricted to≤650℃due to hydrophobic group limitations,hindering high-temperature applications.This study employs zirconium oxychloride precursor and sol-gel methods to explore drying process effects on Zr-based and Zr/Si composite aerogels.Re-sults demonstrate both materials exhibit high specific surface area,low thermal conductivity,and exceptional heat resistance,showing potential for cement kilns and refractory material calcination-molding processes.
作者
王深成
刘德嵩
林鑫
聂文琪
Wang Shencheng;Liu Desong;Lin Xin;Nie Wenqi(Anhui Conch Siam Refractory Co.,Ltd.,Anhui,241000;Anhui Conch Group Co.,Ltd.,Anhui,241000;Anhui Polytechnic University,Anhui,241000)
出处
《当代化工研究》
2025年第9期182-184,共3页
Modern Chemical Research
基金
安徽省高等学校科学研究项目“‘双碳’背景下耐高温气凝胶隔热材料的研发”(项目编号:2023AH050952)。
关键词
气凝胶
耐高温
双碳
aerogel
high temperature resistant
carbon peak carbon neutrality