Solid-state batteries(SSBs) with high safety are promising for the energy fields,but the development has long been limited by machinability and interfacial problems.Hence,self-supporting,flexible Nano LLZO CSEs are prepared with a solvent-free method at 25℃.The 99.8 wt% contents of Nano LLZO particles enable the Nano LLZO CSEs to maintain good thermal stability while exhibiting a wide electrochemical window of 5.0 V and a high Li~+ transfer number of 0.8.The mean modulus reaches 4376 MPa.Benefiting from the interfacial modulation,the Li|Li symmetric batteries based on the Nano LLZO CSEs show benign stability with lithium at the current densities of 0.1 mA cm^(-2),0.2 mA cm^(-2),and 0.5 mA cm^(-2).In addition,the Li|LiFePO_(4)(LFP) SSBs achieve favorable cycling performance:the specific capacity reaches128.1 mAh g^(-1) at 0.5 C rate,with a capacity retention of about 80% after 600 cycles.In the further tests of the LiNi_(0.8)Co_(0.1)Mn_(0.1)O_(2)(NCM811) cathodes with higher energy density,the Nano LLZO CSEs also demonstrate good compatibility:the specific capacities of NCM811-based SSBs reach 177.9 mAh g^(-1) at 0.5 C rate,while the capacity retention is over 96% after 150 cycles.Furthermore,the Li|LFP soft-pack SSBs verify the safety characteristics and the potential for application,which have a desirable prospect.
基金
supported by Science and Technology Project of China Southern Power Grid (SZKJXM20230049/090000KC23010038)。