以废弃文冠果壳为原料制备液体地膜并考察其保水及保温性能。结果表明:液体地膜的—OH和—COOH基团可被土壤微生物所降解,埋入土壤12 d后,液体地膜表面呈现出的孔洞和收缩现象,距土壤表面8 cm处温度升高3.5℃左右。通过含水率对比试验时发现,液体地膜的覆盖可显著提高土壤的含水率。液体地膜的表面接触角为47.6°,抗拉强度为16.69 MPa,黏度为35.6 mPa·s,12 d后降解率达3.7%。
Liquid film was prepared from waste Xanthoceras sorbifolia shell and its water retention and thermal insulation properties were investigated.The results showed that the-OH and-COOH groups of the liquid film could be degraded by soil microorganisms.After 12 days of embedding in the soil,the surface of the liquid film showed holes and shrinkage,and the temperature at 8 cm from the soil surface increased by about 3.5℃.Through the comparison experiment of water content,it was found that the coverage of liquid film could significantly increase the water content of soil.The surface contact angle of the liquid film was 47.6°,the tensile strength was 16.69 MPa,the viscosity was 35.6 mPa·s,and the degradation rate was 3.7%after 12 days.
作者
郝一男
王任飞
张国
郑晶茹
王硕
姚利宏
HAO Yi-nan;WANG Ren-fei;ZHANG Guo;ZHENG Jing-ru;WANG Shuo;YAO Li-hong(College of Material Science and Art Design,Inner Mongolia Agricultural University,Hohhot 010018,Inner Mongolia,P.R.China;National Forestry Grassland Engineering Technology Research Center for Efficient Development and Utilization of Sandy Shrubs,Hohhot 010018,Inner Mongolia,P.R.China;Inner Mongolia geology and Mining Ecological Construction Limited liability company,Hohhot 010018,Inner Mongolia,P.R.China;Woqi Ecological Agriculture Limited of Jungar Banner,Ordos 017100,Inner Mongolia,P.R.China)
出处
《林产工业》
北大核心
2025年第2期31-36,共6页
China Forest Products Industry
基金
内蒙古自治区科技计划项目(2022YFDZ0045)
准格尔旗科技计划项目(2023YY-12)
内蒙古自然基金项目(2024MS03068)。
关键词
液体地膜
文冠果壳
可降解性能
保水性能
保温性能
Liquid film
Xanthoceras sorbifolia bunge shell
Degradability
Water retention property
Thermal insulation property