摘要
采用钢渣、水泥、石膏、石灰等为原材料,通过预养护加二氧化碳养护的方式,研究了聚羧酸减水剂对碳化养护加气混凝土产品性能的影响。结果表明:聚羧酸减水剂对碳化养护加气混凝土的流变性能、干密度、抗压强度及固碳量具有较大影响,聚羧酸减水剂掺量由0.60%逐渐增大到0.76%,碳化养护加气混凝土测试样的屈服应力及固碳量逐渐增大,干密度及强度逐渐降低。此外,减水剂掺量0.72%时,碳化养护加气混凝土综合性能最优,此时,干密度为621kg/m^(3),抗压强度为4.0MPa,固碳量为11.52%。
By means of precuring and carbon dioxide curing,this paper studied the effects of polycarboxylate superplasticizer on the properties of carbonized cured aerated concrete products by taking steel slag,cement,gypsum,lime,etc.as raw materials.The results showed that:polycarboxylate superplasticizer had a significant impact on the rheological properties,dry density,compressive strength,and carbon fixation of carbonized cured aerated concrete.The dosage of polycarboxylate superplasticizer gradually increased from 0.60% to 0.76%,and the yield stress and carbon fixation of carbonized cured aerated concrete test samples gradually increased,while the dry density and compressive strength gradually decreased.In addition,when the dosage of polycarboxylate superplasticizer was 0.72%,the compressive strength of carbonized cured aerated concrete was optimal.At this time,the dry density was 621 kg/m^(3),the compressive strength was 4.0 MPa,and the carbon fixation was 11.52%.
作者
王奕杰
周凤娇
谭新宇
张宾
陶从喜
邓恺
Wang Yijie;Zhou Fengjiao;Tan Xinyu;Zhang Bin;Tao Congxi;Deng Kai(China Resources Cement Technology Research and Development(Guangxi)Co.,Ltd.,Nanning,530000,China)
出处
《水泥工程》
2024年第6期85-89,共5页
Cement Engineering
关键词
聚羧酸减水剂
二氧化碳
抗压强度
固碳
polycarboxylate superplasticizer
carbon dioxide
compressive strength
carbon fixation