二氧化钒微结构的光场调控性能 被引量:3

Light Field Manipulation Properties of Vanadium Dioxide Microstructure
原文传递
导出
摘要 随着纳米技术和材料科学的发展,二氧化钒微结构的制备、性质调控和应用受到广大科研人员的高度关注,且二氧化钒微结构的光场调控性能在光化学性能、光学传感和光电子器件等方面有巨大的研究前景。为了更好地研究二氧化钒微结构的光场调控性能,本文采用成本低、工艺简单的人工方法制备成二氧化钒微结构,并对制得样品的激光衍射图样、近红外光谱测试结果等进行了深入的研究和讨论。 Objective In recent years,with the development of nanotechnology,research on vanadium dioxide(VO2)microstructures focuses on preparation,property control,and application,particularly in areas such as smart windows,storage devices,and optoelectronic devices.The light field control performance of VO2 microstructures has shown great potential in fields like photocatalysis,optical sensing,and optoelectronic devices.Currently,the mainstream preparation methods include solution methods and thermal decomposition methods,but they have drawbacks such as complex processes.We employ a self-assembly method to prepare tungsten-doped VO2 microstructures and thoroughly explore their light field control performance to achieve practical applications.Methods A homemade circular polystyrene(PS)mold with a diameter of 10.0 mm and a thickness of 2.0 mm is placed on a clean and level desk.Adhesive tape is applied on the desktop beneath and above the mold,and the polyethylene(PE)lines are cut into long and short threads,which are then interlaced densely on the mold and fixed at both ends with tape.After securing the mold,it is flipped,and two drops of nanosolution with a W-doped atomic ratio of 2%are dripped from 1 to 2 cm above the mold,waiting for it to solidify.Once solidified,the long thread is carefully separated from the microstructure,leading to W_(x)V_(1-x)O_(2)/glass microstructures under different numbers of PE lines.Finally,the sample made with nanosolution with a W-doped atomic ratio of 2%and 9 PE lines exhibits sound symmetry,clarity,integrity,and uniformity.The above experiment is repeated by utilizing W_(x)V_(1-x)O_(2) nanosolution with a W-doped atomic ratio of 2%and 9 PE lines,with the formation process of the W_(x)V_(1-x)O_(2)/glass microstructure recorded.The solution first spreads outward to the edges of the homemade experimental mold,with the relatively thin center of the solution and relatively thick edges.The PE lines form symmetrical crescent-shaped films,which gradually thicken inward.Subsequently,the surface morphology of the film samples is tested by adopting the German ZEISS GeminiSEM 300 scanning electron microscope.Then,a testing platform is set up by employing a 980 nm wavelength laser,with the optical path shown in Fig.4.Thermal-sensitive paper is adopted to help align the optical path,ensuring that the laser passes through the film.Meanwhile,a helium-neon(He-Ne)laser is utilized to replace near-infrared light to assist in observing diffraction patterns.Results and Discusses On the set-up near-infrared light transmittance measurement device,by replacing the light detector with a screen and the infrared light with a He-Ne laser,distinct moirépatterns can be observed for the nine vertically aligned W_(x)V_(1-x)O_(2)/glass microstructures.After appropriately adjusting the relative position of the light-emitting device and the VO2 microstructure,the moirépatterns can be observed.By keeping the horizontal distance between the light source and the microstructure unchanged,and adjusting the vertical relative position of the light source and the W_(x)V_(1-x)O_(2)/glass microstructure,it is possible to observe whether moirépatterns form.Additionally,the vertical adjustment between the light source and the W_(x)V_(1-x)O_(2)/glass microstructure is achieved by utilizing the LD-60-CM(XYZaxis)high-precision manual displacement stage.For the cross and asterisk VO2 microstructures,the diffraction fringes can be observed to change as the relative vertical position between the light source and the W_(x)V_(1-x)O_(2)/glass microstructure is altered.Meanwhile,the diffraction patterns show two types of stripes intersecting to form a cross at times and alternating patterns at other times.Based on the diffraction patterns of the cross and asterisk W_(x)V_(1-x)O_(2)/glass film microstructures under red laser light,we can observe that compared to the patterns of the 9 W_(x)V_(1-x)O_(2)/glass thin film microstructures under visible light,both the cross and asterisk W_(x)V_(1-x)O_(2)/glass microstructures show intersecting grid patterns,which are moirépatterns produced by the grating superposition.Computer simulation of moirépatterns is realized by adopting Python code.The transmittance data of different W_(x)V_(1-x)O_(2)/glass thin films and microstructures at different temperatures are obtainedvia a variable-temperature infrared testing platform.Conclusions We innovatively fabricate the W_(x)V_(1-x)O_(2)/glass thin film microstructure by employing a simple and feasiblemethod of mold preparation. By observing and testing the optical properties of the W_(x)V_(1-x)O_(2)/glass microstructure, weconclude that the sample with a W-doped atomic ratio of 2% has better formation and light field control performance.Furthermore, cross and asterisk microstructures are designed, and a He-Ne laser is adopted as the light source to obtaindiffraction patterns. After light passes through the W_(x)V_(1-x)O_(2)/glass microstructure, diffraction phenomena occur, and it isobserved that within a certain range, adjusting the relative position of the light source to the vertical direction of themicrostructure allows the observation of changes in the diffraction pattern of the microstructure. A self-built variabletemperatureinfrared testing platform is adopted to achieve control of the diffraction pattern direction, and the computersimulation of the moiré patterns generated by the grating superposition is consistent with the experimental results. Thisdemonstrates that the optical properties of the W-doped VO2 microstructure prepared by a simple, low-cost, and easy-toimplementmethod can be quantitatively controlled. We will focus on developing devices that can finely control the lightfield control performance of the W_(x)V_(1-x)O_(2)/glass microstructure in subsequent studies to achieve industrial applications.
作者 张钧 杨文俊 李磊 张笑然 朱亚彬 Zhang Jun;Yang Wenjun;Li Lei;Zhang Xiaoran;Zhu Yabin(Department of Physics,School of Physical Sciences and Engineering,Beijing Jiaotong University,Beijing 100044,China)
出处 《光学学报》 CSCD 北大核心 2024年第22期10-17,共8页 Acta Optica Sinica
关键词 掺钨二氧化钒 WxV1-xO2/glass微结构 透过率 衍射图样 数字模拟 tungsten-doped vanadium dioxide WxV1-xO2/glass microstructure transmittance diffraction pattern digital simulation
  • 相关文献

参考文献9

二级参考文献64

  • 1张正华,徐伟箭,刘含茂.反饱和吸收光限幅效应与激光防护[J].精细化工中间体,2005,35(5):51-54. 被引量:5
  • 2宋华,杨东明,李锋,刘全夫,徐骞.SO_4^(2-)/M_xO_y型固体超强酸催化剂的研究进展[J].化工进展,2007,26(2):145-151. 被引量:49
  • 3顾去吉.莫尔现象,干涉术和全息术[J].光学学报,1981,1(2):35-40.
  • 4顾杰,沈永昭,姜锦虎.散斑全场分析的moire理论[J]中国激光,1987(10).
  • 5Y.Li,F.Ma,N.Dai,G.Yang,P.Lu. Chinese Journal of Lasers . 2007
  • 6L.Yuan,Y.Zhao,H.He,J.Shao. Chin.Opt.Lett . 2007
  • 7Y.Cui,H.Yu,Y.Zhao,Y.Jin,H.He,J.Shao. Chin. Opt.Lett . 2007
  • 8H.Sun,T.Jia,C.Li,X.Li,S.Xu,D.Feng,X.Wang,X.Ge,Z.Xu. Solid State Communications . 2007
  • 9S.Xu,T.Jia,X.Li,D.Feng,H.Sun,C.Li,X.Wang,H.Kuroda,R.Li,Z.Xu. Japanese Journal of Applied Physics . 2005
  • 10Z.Xia,J.Shao,Z.Fan. Chinese J.Mater.Res . 2006

共引文献23

同被引文献17

引证文献3

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部