摘要
We prepared Au/Ag core-shell nanoparticles by growing Ag shell onto 12 nm Au core, using silver nitrate and sodium citrate as the reactants. By changing the molar ratio of Ag to Au, the shell thickness and thus the size of bimetallic particles could be controlled in convenient way. The formation of core-shell structure was proved by UV-Vis spectra, transmission electron microscopy(TEM), etc.. The core-shell particles showed a more narrow size distribution than Ag colloid prepared without Au core. The SERS activity of the core-shell particles was investigated by using 2,4-dimethylpyridine as the probe, which strongly indicated their potential application in SERS substrate materials.
We prepared Au/Ag core-shell nanoparticles by growing Ag shell onto 12 nm Au core, using silver nitrate and sodium citrate as the reactants. By changing the molar ratio of Ag to Au, the shell thickness and thus the size of bimetallic particles could be controlled in convenient way. The formation of core-shell structure was proved by UV-Vis spectra, transmission electron microscopy(TEM), etc.. The core-shell particles showed a more narrow size distribution than Ag colloid prepared without Au core. The SERS activity of the core-shell particles was investigated by using 2,4-dimethylpyridine as the probe, which strongly indicated their potential application in SERS substrate materials.
出处
《高等学校化学学报》
SCIE
EI
CAS
CSCD
北大核心
2002年第12期2357-2359,共3页
Chemical Journal of Chinese Universities
基金
国家自然科学基金 (批准号 :2 0 0 730 16 )
"九七三"项目 (批准号 :G19990 6 45 0 4)资助