摘要
The high-entropy alloy(HEA)superconductor,Ta_(1/6)Nb_(2/6)Hf_(1/6)Zr_(1/6)Ti_(1/6)(Ta-Nb-Hf-Zr-Ti),is systematically studied to examine changes in superconducting critical properties,critical temperature(T_(c)),critical cur-rent density(J_(c)),and upper critical field(H_(c2)),concerning thermal treatment conditions.Annealing condi-tion affects Jc more significantly than T_(c)and H_(c2),with a large improvement of flux pinning force density(F_(p)).The Jc of bare sample is reduced to 10 A cm^(-2)at an applied magnetic field of approximately 1.5 T,whereas the sample annealed at 550℃for 12 h exhibits J_(c)>100 kA cm^(-2)up to around 4 T.Furthermore,the Vickers hardness(HVIT)of the Ta-Nb-Hf-Zr-Ti HEA superconductor notably increases from∼384 to 528 HVIT following a 24-h annealing at 500℃.These results demonstrate that thermal annealing is a powerful process to optimize both the superconducting and mechanical properties of high-entropy alloy superconductors.
基金
supported by the National Research Foundation of Korea(NRF)grant funded by the Korean government(MIST)(Nos.2021R1A2C2010925,RS-2023-00240326,and RS-2023-00220471)
Basic Science Research Program through the NRF of Korea funded by the Ministry of Education(Nos.NRF-2019R1F1A1055284 and NRF-2021R1I1A1A01043885).