摘要
Submerged entry nozzle(SEN)clogging is a major problem affecting the production quality of rare earth steel,and finding a suitable refractory outlet can significantly reduce production costs.To explore the relationship between refractory composition and interface interaction,unprotected coated Al_(2)O_(3)–MgO refractories and SiO2-coated Al_(2)O_(3)–MgO refractories were added to rare earth high-carbon heavy rail steel under laboratory conditions,and the Al_(2)O_(3)–MgO refractory was found to be more suitable.The results show that,from the epoxy resin side to the refractory side,the contour of the refractory interface reaction layer can be divided into two main layers:an iron-rich reaction layer and an iron-poor reaction layer.Calculations based on the spherical model suggest that the adhesion force is proportional to the size of the refractory particles and inclusions,and the same result applies to the surface tension.Controlling the inclusions at a smaller size has a specific effect on alleviating the erosion of refractories.Combined with the erosion mechanism of Al_(2)O_(3)–MgO refractories,the interface reaction mechanism between Al_(2)O_(3)–MgO refractories and molten steel was proposed,which provides ideas for solving SEN clogging.
基金
the State Key Laboratory of Rare Earth Resources Research and Comprehensive Utilization of Baiyun Obo for the open project(Grant No.2022(Kehe)00281)
the Central Government Guidance Local Science and Technology Development Fund Project(Grant No.2022ZY0124)for supporting this work
supported by the National Natural Science Foundation of China(Grant No.52074179).