摘要
A block copolymer of PDMS-b-PGMA is synthesized by polymerizing glycidyl methacrylate(GMA)via reversible addition-fragmentation chain transfer(RAFT)polymerization applying a polydimethylsiloxane(PDMS)based macro-RAFT agent,which is then performed to functionalize the quartz fibers(QFs@PDMS-b-PGMA)via a simple coating process.Finally,the QFs@PDMS-b-PGMA/bisphenol A dicyanate ester(BADCy)wave-transparent laminated composites are fabricated by high-temperature molding.Nuclear magnetic resonance(NMR)spectroscopy,Fourier transform infrared(FT-IR)spectroscopy and size ex-clusion chromatography(SEC)demonstrate the successful preparation of PDMS-b-PGMA with expected structure.When the molar mass and coating amount of PDMS-b-PGMA are respectively 8100 g/mol and 2.0 wt.%,QFs@PDMS-b-PGMA/BADCy wave-transparent laminated composites present optimal mechan-ical properties and wave-transparent performance.The interlaminar shear strength(ILSS)and flexural strength are 53.6 and 552.0 MPa,respectively.Meanwhile,the dielectric constant and dielectric loss val-ues are 2.61 and 0.0028 at 1 MHz(wave transmittance of 93.8%),showing good stability at different frequencies(102-106 Hz and 8.4-12.4 GHz)and temperatures(25-250℃).