摘要
采用锑碳复合材料作为负极活性材料组装纽扣锂离子电池,对其进行准静态平板和接触(钢球)挤压加载实验,研究其在载荷作用下的电化学循环稳定性、电极表面裂纹及其失效。结果表明,在0~960 N的范围内,接触压缩载荷和准静态平板载荷均会对电池容量造成损伤,随着载荷增大,电极表面裂纹越大,活性材料剥落越多,导致可逆容量损失越大。接触压缩载荷作用后,电池外壳出现凹陷,电极表面形成较大裂纹,导致电池可逆容量大幅度下降,循环稳定性差;准静态平板载荷作用后,电池可逆容量损失较小,循环稳定性没有明显变化,归因于电池外壳的保护作用。该研究为锑碳负极材料在压缩载荷作用下的失效提供了参考。
Antimony carbon composite was used as active materials in the anode to assemble button lithium-ion batteries(LIBs),and quasi-static plate and contact(steel balls)extrusion loading experiments were carried out.The cycling stability,crack morphology of electrode,and failure of LIBs were investigated.The results indicate the quasi-static plate and contact(steel balls)extrusion load cause the decrease of reversible capacity,and the reversible capacity loss is positively correlated with quasi-static plate and contact load compression load,which can be attributed to increased width of cracks and peeling off of active materials with increasing compression load in the range of 0-960 N.In addition,the contact compression load causes lagre reversible capacity decrease and poor cycling performance,which can be related to large cracks,concave area,and fracture on the electrode formed under contact compression load.The quasi-static plate load causes little reversible capacity loss and no obvious decease of cycling performance,which is attributed to the protective effect of the battery shell.These conclusions provide a reference for the failure study of antimony carbon anode materials under mechanical load.
作者
孙维岩
孟伟嘉
赵松楠
郭春丽
郭美卿
SUN Weiyan;MENG Weijia;ZHAO Songnan;GUO Chunli;GUO Meiqing(College of Mechanical and Vehicle Engineering,Taiyuan University of Technology,Taiyuan 030024,China;College of Materials Science and Engineering,Taiyuan University of Technology,Taiyuan 030024,China;Key Laboratory of Material Strength and Structure Impact in Shanxi Province,Taiyuan University of Technology,Taiyuan 030024,China)
出处
《太原理工大学学报》
CAS
北大核心
2023年第3期425-431,共7页
Journal of Taiyuan University of Technology
基金
中央引导地方科技发展项目(自由探索类基础研究:YDZJSX2021A021)
山西省归国留学人员基金资助项目(2020-048)。
关键词
锂离子电池
锑碳负极
准静态平板载荷
接触载荷
lithium-ion battery
antimony carbon anode
quasi-static plate load
contact load