摘要
Iron-based catalysts have been explored for selective catalytic reduction(SCR)of NO due to environmentally benign characters and good SCR activity.Mn-W-Sb modified siderite catalysts were prepared by impregnation method based on siderite ore,and SCR perfor-mance of the catalysts was investigated.The catalysts were analyzed by X-ray diffrac-tion,H_(2)-temperature-programmed reduction,Brunauer-Emmett-Teller,Thermogravimetry-derivative thermogravimetry and in-situ diffused reflectance infrared Fourier transform spectroscopy(DRIFTS).The modified siderite catalysts calcined at 450℃ mainly consist of Fe_(2)O_(3),and added Mn,W and Sb species are amorphous.3Mn-5W-1.5Sb-siderite catalyst has a wide temperature window of 180-360℃ and good N_(2) selectivity at low temperatures.In-situ DRIFTS results show NH_(4)^(+),coordinated NH_(3),NH_(2),NO_(3)^(-)species(bidentate),NO_(2)-species(nitro,nitro-nitrito,monodentate),and adsorbed NO_(2) can be discovered on the sur-face of Mn-W-Sb modified siderite catalysts,and doping of Mn will enhance adsorbed NO_(2) formation by synergistic catalysis with Fe^(3+).In addition,the addition of Sb can inhibit sulfates formation on the surface of the catalyst in the presence of SO_(2) and H_(2)O.Time-dependent in-situ DRIFTS studies also indicate that both of Lewis and Br?nsted acid sites play a role in SCR of NO by ammonia at low temperatures.The mechanism of NO removal on the 3Mn-5W-1.5Sb-siderite catalyst can be discovered as a combination of Eley-Rideal and Langmuir-Hinshelwood mechanisms with three reaction pathways.The mechanism of NO,oxidized by synergistic catalysis of Fe^(3+)and Mn^(4+/3+)to form NO_(2) among three pathways,reveals the reason of high NO_(x) conversion of the catalyst at medium and low temperatures.
基金
This work was supported by the National Natural Science Foundation of China(Nos.51406077 and 51276039).