摘要
针对输水及热力管线大直径厚壁螺旋埋弧焊管生产过程中,保留钢带对接焊缝出现的裂纹缺陷问题,结合钢带对接埋弧焊的工艺和设备特点,分析了裂纹产生的原因。分析指出,钢带对接焊缝裂纹主要是由于焊缝中低熔点夹杂物、焊缝熔池的拘束应力和热轧钢卷板材头尾部分未矫平、在合缝对焊时产生的变形应力以及剪切头尾断面存在超过70%的撕裂等现象的影响。最后提出了避免裂纹产生的措施。
Aiming at the production of large diameter thick-wall spiral submerged arc welding pipe of water and heat transmission pipeline,the crack defects of steel belt butt welding are preserved,and the causes of crack are analyzed in combination with the technology and equipment characteristics of butt welding.The analysis show that the crack of steel belt butt welding is mainly due to the low melting point inclusion in the weld,the constraint stress of the weld pool,the non-straightening and leveling of the head and tail parts of the hot-rolled coil sheet,the deformation stress generated during the joint welding,and the tearing of over 70%of the shear head and tail section.The measures to avoid cracks are put forward.
作者
雷浩
胡德虎
高鹏
曹文军
LEI Hao;HU Dehu;GAO Peng;CAO Wenjun(Baoji Petroleum Steel Pipe Co.,Ltd.,Baoji 721008,Shaanxi,China)
出处
《焊管》
2020年第9期51-55,59,共6页
Welded Pipe and Tube
关键词
螺旋埋弧焊管
对接焊焊缝
热裂纹
钢带矫平
拘束应力
剪切断面
焊缝余高
spiral submerged arc welding pipe
butt weld
hot crack
strip leveling
confining stress
shear section
weld reinforcement