In this work,coarse-grained 316 L stainless steels were cold rolled with a thickness reduction of^83%(CR 83%).After annealing,the behaviors of the nanostructured stainless steel samples were systematically investigated in the temperatures range of 200C–650C.It was found that with increasing annealing temperature the volume fraction of theα0-martensite first increased to reach a maximum value at 400C,then the volume fraction decreased with further increases of the annealing temperature.The yield strength was increased from 1400 MPa to 1720 MPa after annealing;this strong hardening effect in cold rolled 316 L stainless steel was mainly attributed to the increase of the volume fraction ofα0-martensite.