摘要
To fulfill the high-quality surface requirements of the Fe-36% Ni cold-rolled strip used in liquid natural gas carriers,corrosion tests were conducted on alloy surfaces using ink media with different composition in hightemperature and high-humidity conditions.The results show that the Cl^-content in ink is the main cause of surface corrosion of Fe-36%Ni alloy at 95%RH and 50℃ Cl^- penetrates the passivation film,causing pitting on the surface.This corrosive material primarily comprises elements Fe and O.After 120 h of high temperature and high humidity,pitting had occurred on the surface,which was characterized by irregularly distributed areas of bright red filamentous corrosion.With time,the corrosion gradually deepened and expanded to nearby areas.However,when the ink medium contained no Cl^-,no corrosion was found on the alloy surface.As such,during the production of Fe-36%Ni material and its application in LNG shipbuilding,care must be taken in the selection of the marker or medium that will come into contact with the strip surface to ensure that it contains no corrosive ions like Cl^-.