摘要
采用金相显微镜和电子背散射衍射(EBSD)技术分析了楔横轧制备的GH4169合金轧件的微观组织演变和动态再结晶机制;利用数值分析方法获得了楔横轧过程中等效应变、应变速率和温度的相互关系和变化规律,并探讨对楔横轧GH4169合金动态再结晶的影响。结果表明,楔横轧的变形特点是导致GH4169合金组织均匀和动态再结晶机制不同的主要原因,较大的断面收缩率有利于组织均匀化;轧件表面以非连续动态再结晶机制为主,而心部以连续动态再结晶机制为主。
The microstructure evolution and dynamic recrystallization mechanism of GH4169 alloy rolled by cross wedge rolling were characterized by metallographic microscope and electron backscatter diffraction(EBSD).The effects of equivalent strain,strain rate and temperature on the dynamic recrystallization of GH4169 alloy during cross wedge rolling were investigated by numerical analysis.The results reveal that the shaping characteristics of cross wedge rolling are the main reasons that induce the homogeneous microstructure and different dynamic recrystallization mechanisms of GH4169 alloy.Larger reduction of area is beneficial to improving the microstructure homogenization.The non-continuous dynamic recrystallization mechanism is the main form on the surface of the rolled piece,while the core is dominated by continuous dynamic recrystallization mechanism.
作者
甘洪岩
程明
宋鸿武
陈岩
张士宏
Vladimir Petrenko
Gan Hongyan;Cheng Ming;Song Hongwu;Chen Yan;Zhang Shihong;Vladimir Petrenko(Institute of Metal Research,Chinese Academy of Sciences,Shenyang 110016,China;University of Science and Technology of China,Shenyang 110016,China;Physical-Technical Institute of the National Academy of Sciences of Belarus,Minsk 220141,Belarus)
出处
《稀有金属材料与工程》
SCIE
EI
CAS
CSCD
北大核心
2019年第11期3556-3562,共7页
Rare Metal Materials and Engineering
基金
国家自然科学青年基金(51505240)
关键词
GH4169合金
楔横轧
微观组织
动态再结晶
GH4169 alloy
cross wedge rolling
microstructure
dynamic recrystallization