研究了临界区退火温度和退火时间对含δ铁素体的Mn-Al系冷轧TRIP钢(Fe-0.18C-6.4Mn-2.8Al)的组织和性能演变行为的影响。结果表明,随着临界区退火温度的提高和退火时间的延长,实验钢的残余奥氏体(RA)含量和强塑积呈现先增大后减小的趋势。在750℃退火2 min实验钢的组织由δ铁素体、临界区铁素体及残余奥氏体组成,其RA含量为24.7%,抗拉强度为773 MPa,断后延伸率39.4%,强塑积为30.46 GPa·%。RA主要集中在粗大δ铁素体与原马氏体边界、原马氏体区域内再结晶铁素体晶界周围以及粗大δ铁素体内的亚晶界附近。
The microstructure evolution and mechanical properties of a cold-rolled Mn-Al transformation-induced plasticity（TRIP）steel with d ferrite were investigated after annealed at different intercritical annealing temperature for different time.The results show that as the intercritical annealing temperature and time going up,the content of retained austenite（RA）and the product of strength and elongation（PSE）increased first and then decrease.The microstructure of the steel after annealing at 750℃ for 2 min consists of δ ferrite,intercritical ferrite and 24.7% retained austenite,which exhibited a tensile strength of 773 MPa,elongation of 39.4% and the product of strength and elongation of 30.46 GPa·%.RA mainly exits at the boundaries between bulky δ ferrite and original martensite,around the recrystallization ferrite from original martensite area,and around the sub-grain boundaries inside δ ferrite.
作者
胡智评
许云波
刘慧
王乐
HU Zhiping;XU Yunbo;LIU Hui;WANG Le(State Key Laboratory of Rolling andAutomation, Northeastern University, Shenyang 110819, China;Research InstituteofIron and Steel of Shandong Iron and Steel Group, Jinan 250101, China)
出处
《材料研究学报》
EI
CAS
CSCD
北大核心
2018年第3期177-183,共7页
Chinese Journal of Materials Research
基金
国家自然科学基金(51174059
51404155
U1260204)
中央高校基本科研业务费项目(N130407003)
新世纪优秀人才支持计划(NCET-13-0111)
辽宁省高等学校优秀人才支持计划(LR2014007)~~