摘要
The sintering of chromium-containing vanadium-titanium magnetite using different coke contents was studied through the sintering pot tests, X-ray diffraction analysis and mineralogical phase analysis. Results showed that, as the coke content increased from 3.2% to 4.4%, the liquid phase and combustion zone thickness increased while the vertical sintering rate and ratio of sintered product decreased. In addition, the combustion ratio of exhaust gas also increased with increasing the coke content, indicating that combustion zone temperature also increased, and the excessive the coke content in the sintering process of vanadiumtitanium magnetite is harmful. As the coke content increased, the magnetite, silicates, and perovskite contents of the sintered ore increased while the contents of hematite and calcium ferrite of sintered ore decreased; drum strength decreased, and reduction degradation properties increased while reduction ability decreased. We found that the appropriate coke content for the sintering process is 3.6 wt%.
The sintering of chromium-containing vanadium-titanium magnetite using different coke contents was studied through the sintering pot tests, X-ray diffraction analysis and mineralogical phase analysis. Results showed that, as the coke content increased from 3.2% to 4.4%, the liquid phase and combustion zone thickness increased while the vertical sintering rate and ratio of sintered product decreased. In addition, the combustion ratio of exhaust gas also increased with increasing the coke content, indicating that combustion zone temperature also increased, and the excessive the coke content in the sintering process of vanadiumtitanium magnetite is harmful. As the coke content increased, the magnetite, silicates, and perovskite contents of the sintered ore increased while the contents of hematite and calcium ferrite of sintered ore decreased; drum strength decreased, and reduction degradation properties increased while reduction ability decreased. We found that the appropriate coke content for the sintering process is 3.6 wt%.
基金
Funded by the National Natural Science Foundation of China(Nos.51604065,51674084)
the Fundamental Funds for the Program of the Science Foundation of Liaoning Province(No.20170540316)