摘要
A novel processing route involving strip casting, pre-annealing treatment, cold rolling and recrystallization annealing was applied to a Fe-2.6%Si steel to improve the magnetic properties. The impact of as-cast strip pre-annealing on the microstructure, texture, precipitation and magnetic properties were investigated by electron probe micro-analysis, transmission electron microscopy, and X-ray diffraction analysis,etc. It was found that the precipitation of second-phase particles during strip casting was restrained by rapid solidification. The absence of pre-annealing led to the occurrence of a large amount of 20-50 nm Mn S precipitates in the final annealed sheets, which is responsible for fine grains and high core loss（4.01 W/kg） due to grain boundary pinning effect. Although the microstructure and texture of 900-1000？C pre-annealed samples were similar to those of as-cast strip, significant grain coarsening together with the strengthening of-fiber texture was observed in the 1100？C pre-annealed strips. In comparison with the case of as-cast strip, a higher amount of large-sized precipitates consisting of manganese sulfide and/or aluminum nitride occurred in matrix after pre-annealing. Correspondingly, in the final annealed sheets, the number density of precipitates with sizes smaller than 100 nm was substantially reduced, and100-200 nm and 200-500 nm sized particles became more dominant in samples subjected to 30-min and 120-min pre-annealing treatments respectively. In addition, the average grain size of final annealed sheets increased with the pre-annealing temperature and time because of the weakened pining effect of coarsen precipitates. Ultimately, the magnetic induction of samples subjected to pre-annealing was slightly increased and ranged from 1.73 T to 1.75 T owing to the enhancement of {100} recrystallization texture, and simultaneously the core loss significantly decreased until a minimum of 3.26 W/kg was reached. Nevertheless, large number of 200-500 nm particles presented during pre-annealing for 120 min could weaken the improvement in core loss which is likely associated with the pinning effect on magnetic domain wall.
A novel processing route involving strip casting, pre-annealing treatment, cold rolling and recrystallization annealing was applied to a Fe-2.6%Si steel to improve the magnetic properties. The impact of as-cast strip pre-annealing on the microstructure, texture, precipitation and magnetic properties were investigated by electron probe micro-analysis, transmission electron microscopy, and X-ray diffraction analysis,etc. It was found that the precipitation of second-phase particles during strip casting was restrained by rapid solidification. The absence of pre-annealing led to the occurrence of a large amount of 20-50 nm Mn S precipitates in the final annealed sheets, which is responsible for fine grains and high core loss（4.01 W/kg） due to grain boundary pinning effect. Although the microstructure and texture of 900-1000？C pre-annealed samples were similar to those of as-cast strip, significant grain coarsening together with the strengthening of-fiber texture was observed in the 1100？C pre-annealed strips. In comparison with the case of as-cast strip, a higher amount of large-sized precipitates consisting of manganese sulfide and/or aluminum nitride occurred in matrix after pre-annealing. Correspondingly, in the final annealed sheets, the number density of precipitates with sizes smaller than 100 nm was substantially reduced, and100-200 nm and 200-500 nm sized particles became more dominant in samples subjected to 30-min and 120-min pre-annealing treatments respectively. In addition, the average grain size of final annealed sheets increased with the pre-annealing temperature and time because of the weakened pining effect of coarsen precipitates. Ultimately, the magnetic induction of samples subjected to pre-annealing was slightly increased and ranged from 1.73 T to 1.75 T owing to the enhancement of {100} recrystallization texture, and simultaneously the core loss significantly decreased until a minimum of 3.26 W/kg was reached. Nevertheless, large number of 200-500 nm particles presented during pre-annealing for 120 min could weaken the improvement in core loss which is likely associated with the pinning effect on magnetic domain wall.
基金
financially supported by the National Natural Science Foundation of China(Nos.51674080,51404155 and U1260204)
the Program for New Century Excellent Talents in University(No.NCET-13-0111)
the Program for Liaoning Excellent Talents in University(No.LR2014007)
support from the University of Texas at El Paso