摘要
Nitrided hierarchical porous ZSM-5 was synthesized by nitridation of hierarchical porous ZSM-5 with flowing ammonia at elevated temperature.The samples were characterized by XRD,SEM,Nitrogen sorption isotherms,NH3-TPD and Py-IR,and evaluated in alkylation of benzene and methanol.The result indicated that the high specific surface area of parent ZSM-5 was maintained,while the Bronsted acidity was effectively adjusted by nitridation.Moreover,the high suppression of ethylbenzene was observed on nitrided catalyst and this could be attributed to the decrease of Bronsted acidity which suppressed the methanol to olefins reactions.
Nitrided hierarchical porous ZSM-5 was synthesized by nitridation of hierarchical porous ZSM-5 with flowing ammonia at elevated temperature.The samples were characterized by XRD,SEM,Nitrogen sorption isotherms,NH3-TPD and Py-IR,and evaluated in alkylation of benzene and methanol.The result indicated that the high specific surface area of parent ZSM-5 was maintained,while the Bronsted acidity was effectively adjusted by nitridation.Moreover,the high suppression of ethylbenzene was observed on nitrided catalyst and this could be attributed to the decrease of Bronsted acidity which suppressed the methanol to olefins reactions.
基金
the National Natural Science Foundation of China (Nos. 21476207 and 21506189)
Zhejiang Postdoctoral Research Funded Projects (No. BSH1502147)
National Basic Research Program of China (973 Program, No. 2011CB710800)