Potassium and phosphate were extracted at low temperature by acid hydrolysis process to decompose a new type of associated phosphorus and potassium ore. The main factors affecting the dissolution rate were investigated, such as grinding fineness, the amount of sulfuric acid and fluoride salt, reaction time and temperature, etc. Meanwhile, the effects of various factors on the formation of soluble potassium and phosphate were also discussed. The reaction products and residues were determined by X-ray diffraction（XRD）, scanning electron microscopic（SEM） analysis and other means. The results showed that the dissolution rates of potassium and phosphorus were 70wt% and 93.7wt%, respectively, under the conditions of a grain size of 95.64wt% lessthan 0.074 mm, 9.78 g·g^（-1） sulfuric acid, 0.5 g·g^（-1） ammonium fluoride, 160 ℃ and a reaction time of 2h. The thermodynamic and chemical reaction mechanism was revealed that the primary reaction could be completed spontaneously in a temperature range of 298-433 K. The increase of reaction temperature had an important influence on ion exchange reaction, which was more conducive to the spontaneous process. The research will open up a new way for efficient use of potassium ore resources.
Potassium and phosphate were extracted at low temperature by acid hydrolysis process to decompose a new type of associated phosphorus and potassium ore. The main factors affecting the dissolution rate were investigated, such as grinding fineness, the amount of sulfuric acid and fluoride salt, reaction time and temperature, etc. Meanwhile, the effects of various factors on the formation of soluble potassium and phosphate were also discussed. The reaction products and residues were determined by X-ray diffraction（XRD）, scanning electron microscopic（SEM） analysis and other means. The results showed that the dissolution rates of potassium and phosphorus were 70wt% and 93.7wt%, respectively, under the conditions of a grain size of 95.64wt% lessthan 0.074 mm, 9.78 g·g^（-1） sulfuric acid, 0.5 g·g^（-1） ammonium fluoride, 160 ℃ and a reaction time of 2h. The thermodynamic and chemical reaction mechanism was revealed that the primary reaction could be completed spontaneously in a temperature range of 298-433 K. The increase of reaction temperature had an important influence on ion exchange reaction, which was more conducive to the spontaneous process. The research will open up a new way for efficient use of potassium ore resources.
基金
Funded by the National Natural Science Fundation of China(51274158)
the National Twelfth Five-Year Plan for Scientific and Technological Support(2013BAE04B03)
the Scientific and Technological Support Project of Hubei Province(2015BCA251)