摘要
为减小以提盐废卤为基液制备的酸性高密度无固相压井液的腐蚀性,以二乙醇胺、甲醛和苯乙酮为原料采用正交实验法制备了一种适用于该类压井液的醛酮胺类缓蚀剂WX1A,利用失重法、电化学分析和SEM扫描电镜研究了该缓蚀剂对N80、P110钢片在压井液(以p H为3的普钙老水制备的酸性高密度无固相压井液)中不同条件下的缓蚀效果。结果表明:在二乙醇胺、甲醛、苯乙酮摩尔比1.2:2:1.2,反应温度110℃,反应时间10 h,反应p H1条件下合成的缓蚀剂WX1A的缓蚀效果最佳;该缓蚀剂的最佳用量为80 mg/L,在此加量下,当温度从60℃升至80℃,缓蚀剂WX1A对N80钢片和P110钢片的缓蚀率从87.07%和88.09%分别增至93.12%和92.62%;在密度1.6、1.7、1.8 g/cm^3的压井液中,缓蚀剂WX1A对N80钢和P110钢片的缓蚀率均在90%上,在120℃、2 MPa和150℃、4 MPa条件下缓蚀剂WX1A在密度1.6 g/cm^3的压井液中对N80和P110钢片的缓蚀率均达到94%以上。压井液中添加该缓蚀剂后,缓蚀剂通过吸附在金属基体表面形成较为完整的保护膜,自腐蚀电流密度从10-4A/cm^2降低到10-5A/cm^2,降低了压井液对普通碳钢的腐蚀性。
In order to reduce the corrosion of the high-density and solid-free well killing fluid made by the waste acidic brine, a high temperature corrosion inhibitor WX1A was synthesized using diethanolamine, formaldehyde and acetophenone as the raw materials and with the orthogonal experiment method. The performance of the inhibitor WX1A was researched by utilizing weight loss method, electrochemical method and SEM method for the NS0 and Pll0 steel in the well killing fluid （acid high-density and solid-free well killing fluid with pH of 3 made by the ordinary calcium old water）. The results showed that when the molar ratio of the reactant mole ratio of diethanolamine, formaldehyde and acetophenone was 1.2：2： 1.2, the reaction temperature was 110%, reaction time was 10 h and the reaction pH was 1, the obtained corrosion inhibitor WX1A had the best inhibiting effect. When the temperature rose from 60℃ to 80℃ at the best WX1A concentration of 80 mg/L, the inhibition efficiency of WX1A on the N80 and P 110 steel increased from 87.07% and 88.05% to 93.12% and 92.62%, respectively. The inhibition efficiency of WX 1A on the N80 and P 110 steel could reach above 90%, respectively, in the well killing fluid with the density of 1.6, 1.7 and 1.8 g/cm3 at the WX 1A concentration of 80 mg/L. Furtherly, the inhibition efficiency of WX1A on NS0 and P110 steel in the well killing fluid with the density of 1.6 g/cm3 was above 94%, respectively, at the high temperature and pressure of 120℃, 2 MPa and 150℃, 4 MPa. A complete protection film formed on the surface of a metal matrix when the inhibitor WX1A was added in the well killing fluid, and the corrosion electric current reduced from 10-4AJcm2 to 10 5A/cm2, as a result, the corrosion of ordinary steel reduced in the well killing fluid.
作者
王健
王煦
钟志刚
敬雅雪
简璐
谷琦琦
WANG Jian WANG Xu ZHONG Zhigang JING Yaxue JIAN Lu GU Qiqi(Materials Science and Engineering, Southwest Petroleum University, Chengdu, Sichuan 610500, P R of China)
出处
《油田化学》
CAS
CSCD
北大核心
2016年第3期407-411,436,共6页
Oilfield Chemistry
关键词
高密度无固相压井液
醛酮胺类缓蚀剂
N80钢
P110钢
缓蚀率
high-density and solid-free well killing fluid
aldehyde ketone amine corrosion inhibitor
N80 steel
P110 steel
inhibitionefficiency