摘要
针对锌浸渣中锌难于选择性浸出回收的难题,提出硫酸铵焙烧-选择性浸出回收锌的新工艺。该工艺通过硫酸铵焙烧改变锌浸渣中锌铁物相,在浸出过程对锌进行选择性浸出回收。研究硫酸铵加入量、焙烧温度、焙烧时间等工艺参数对铁酸锌分解和锌铁浸出的影响,并获得最佳的工艺参数,即硫酸铵和铁酸锌质量比为4、一段焙烧温度和时间分别为450℃和90 min,二段焙烧温度和时间分别为650℃和60 min。在该条件下,锌浸出率可以达到92.63%,而铁的浸出率仅为2.04%,实现了锌浸渣中锌的选择性浸出。
In order to solve the difficulty of selective leaching zinc from zinc leaching residue （ZLR）, a novel process for recovery zinc from ZLR was developed by ammonia sulfate roasting-selective leaching. The phases of zinc and iron from ZLR were adjusted by roasting with ammonia sulfate before zinc was leached selectively with water. The effects of various parameters, such as ammonium sulfate addition, roasting temperature and time on decomposition rate of zinc ferrite and extractions rates of zinc and iron were investigated. The optimal experimental conditions are gotten as follows： ammonium sulfate to zinc ferrite mass ratio of 4/1, roasting temperature of 450 ℃ and time of 90 min for the first stage, roasting temperature of 650 ℃ and time of 60 min for the second stage. The extraction rate of zinc increases to 92.63% with the 2.04% extraction rate of iron under the optimal experimental conditions. Zinc can be selectively recovered from ZLR by the new process.
出处
《中国有色金属学报》
EI
CAS
CSCD
北大核心
2015年第9期2596-2603,共8页
The Chinese Journal of Nonferrous Metals
基金
国家高技术研究发展计划资助项目(2011AA061003)
湖南省科技重大专项资助项目(2014FJ1011)
湖南省战略金属矿产资源清洁高效利用协同创新中心资助
关键词
锌浸渣
铁酸锌
硫酸铵焙烧
锌回收
zinc leaching residue
zinc ferrite
ammonia sulfate roasting
zinc recovery