摘要
Experimental investigations on mechanical property and durability of sulphoaluminate cement concrete with aggregate gradations according to Fuller distribution are presented in this paper. Compressive strength, water impermeability and resistance capability to sulfate attack of SACC have the same trend of concrete with fine aggregates of Fuller distribution gradation<concrete with coarse aggregates of Fuller distribution gradation<concrete with total aggregates of Fuller distribution gradation. The relationship between bulk density of aggregate and water penetration depth obeyed the second-order polynomial y=0.002x2-6.863 8x +5 862.3, and had a notable correlation R2=0.979 9. The sulphoaluminate cement concrete with total aggregate gradation with Fuller distribution for h=0.50 had the best resistance capability to sulfate attack. It was a second-order polynomial relationship between bulk density of aggregates and water penetration depth of y=0.002x2-6.863 8x+5 862.3 with R2=0.979 9, which indicated notable correlation. The fitting formula between bulk density of aggregates and sulfate resistance coefficient of SACC was y=0.000 5x+0.370 4 with R2=0.958 5.
Experimental investigations on mechanical property and durability of sulphoaluminate cement concrete with aggregate gradations according to Fuller distribution are presented in this paper. Compressive strength, water impermeability and resistance capability to sulfate attack of SACC have the same trend of concrete with fine aggregates of Fuller distribution gradation<concrete with coarse aggregates of Fuller distribution gradation<concrete with total aggregates of Fuller distribution gradation. The relationship between bulk density of aggregate and water penetration depth obeyed the second-order polynomial y=0.002x2-6.863 8x +5 862.3, and had a notable correlation R2=0.979 9. The sulphoaluminate cement concrete with total aggregate gradation with Fuller distribution for h=0.50 had the best resistance capability to sulfate attack. It was a second-order polynomial relationship between bulk density of aggregates and water penetration depth of y=0.002x2-6.863 8x+5 862.3 with R2=0.979 9, which indicated notable correlation. The fitting formula between bulk density of aggregates and sulfate resistance coefficient of SACC was y=0.000 5x+0.370 4 with R2=0.958 5.
基金
Funded by the National Natural Science Foundation of China(No.51302104)
Research Award Fund for Outstanding Young Scientists of Shandong Province(No.BS2012NJ003)
Foundation of University of Jinan(No.XBS1328)