In this work,the viability of Solidago Canadensis L. for cellulose acetate membrane production was tested. The cellulose was extracted from Solidago Canadensis L. stem by organic solvents,and the cellulose diacetate was obtained by acetylization of cellulose. The properties of the intermediate products of cellulose pulp and cellulose diacetate were characterized by FT-IR and XRD. Compared with commercial cellulose diacetate,the properties of cellulose diacetate were similar to those of the commercial cellulose diacetate. The cellulose acetate membrane with desirable pure water flux and rejection rate was obtained from cellulose diacetate by solution casting. The membrane showed favorable hydrophilic property so that it had good anti-pollution performance. The maximum pure water flux of the membrane was 27. 21 m L /( cm2· h) and the maximum rejection rate was 80. 39%. The results demonstrated that the membrane obtained from herbaceous plant: Solidago Canadensis L. had good performance of ultrafiltration.
In this work,the viability of Solidago Canadensis L. for cellulose acetate membrane production was tested. The cellulose was extracted from Solidago Canadensis L. stem by organic solvents,and the cellulose diacetate was obtained by acetylization of cellulose. The properties of the intermediate products of cellulose pulp and cellulose diacetate were characterized by FT-IR and XRD. Compared with commercial cellulose diacetate,the properties of cellulose diacetate were similar to those of the commercial cellulose diacetate. The cellulose acetate membrane with desirable pure water flux and rejection rate was obtained from cellulose diacetate by solution casting. The membrane showed favorable hydrophilic property so that it had good anti-pollution performance. The maximum pure water flux of the membrane was 27. 21 m L /（ cm2· h） and the maximum rejection rate was 80. 39%. The results demonstrated that the membrane obtained from herbaceous plant： Solidago Canadensis L. had good performance of ultrafiltration.