摘要
通过常温下的液相-氧化还原法制备了层状δ-MnO_(2),用X射线衍射、热重分析、傅立叶红外光谱、扫描电子显微镜等对其物理性质进行了表征、并对其在1mol·L^(-1)LiOH和1mol·L^(-1)KOH电解液中的电化学性能进行了研究.实验结果表明,δ-MnO_(2)在扫描速度为1mV·s^(-1)的速度下,电容达到218F·g^(-1),甚至在扫描速率高达500mV·s^(-1)时,仍表现出明显的氧化-还原性能,这表明该δ-MnO_(2)具有大电流快速充放电的特性.
A layer-structured manganese dioxide was synthesized by the liquid oxidation-reductin method at room temperature,and charactericsed by using X-ray diffraction,thermogravimetric analysis,Fourier transform infrared spectroscopy,scanning electron microscope,the electrochemical performance has studied in 1 tool·L^(-1)LiOH and 1 tool·L^(-1)KOH electrolyte.The results shows thatδ-MnO_(2)at a scan rate of 1 mV·s^(-1)the specific capacitance can achievement 218 F·g^(-1).Even the scan rate at 500 mV·s^(-1),still showed significant oxidation-reduction performance,which indicates that theδ-MnO_(2)has a high-current fast charge and discharge characteristics.
作者
于峰
朱杨军
李莉
章磊
温祖标
YU Feng;ZHU Yangjun;LI Li;ZHANG Lei;WEN Zubiao(College of Chemistry and Chemical Engineer,Yiangxi Normal University,Nanchang 330O22,China)
出处
《复旦学报(自然科学版)》
CAS
CSCD
北大核心
2015年第4期522-528,共7页
Journal of Fudan University:Natural Science
基金
国家自然科学基金(21463013)
江西省自然科学基金(20142BAB203013)