To effectively solve the agglomeration problems in the solid state reaction process,pre-adding glucose is adopted to the synthesis of Li Fe PO4/C energy materials using Fe–P waste slag. The average particle grain size of Li FeP O4/C decreases,and the impurities in Li Fe PO4/C composites reduce to a great extent. It makes great sense to the mass industrial production. The optimum synthesis conditions determined in this work are based on the orthogonal experiments. The samples synthesized in a scale of 500 g exhibit high purity,excellent electrochemical performance,high reaction activity,good reversibility,and low polarization level.The discharge capacities are 145,134,117,and 102 m Ah/g at the current densities of 0.1 C,0.2 C,0.5 C and1 C,respectively. This work puts forward a practical suggestion for mass producing environmental benign and low cost Li FeP O4/C as cathode materials of lithium ion batteries.
To effectively solve the agglomeration problems in the solid state reaction process,pre-adding glucose is adopted to the synthesis of Li Fe PO4/C energy materials using Fe–P waste slag. The average particle grain size of Li FeP O4/C decreases,and the impurities in Li Fe PO4/C composites reduce to a great extent. It makes great sense to the mass industrial production. The optimum synthesis conditions determined in this work are based on the orthogonal experiments. The samples synthesized in a scale of 500 g exhibit high purity,excellent electrochemical performance,high reaction activity,good reversibility,and low polarization level.The discharge capacities are 145,134,117,and 102 m Ah/g at the current densities of 0.1 C,0.2 C,0.5 C and1 C,respectively. This work puts forward a practical suggestion for mass producing environmental benign and low cost Li FeP O4/C as cathode materials of lithium ion batteries.
基金
supported by the National Science Foundation of China(grant no.21206099)