摘要
研究全钢载重子午线轮胎硫化工艺的优化。结果表明:优化工艺的硫化温度和硫化压力不变,硫化时间可缩短7 min,成品轮胎胶料物理性能、带束层间粘合强度相当,耐久性能提高;优化硫化工艺稳定性好,可显著提高生产效率。
In this study, the TBR tire vulcanization process was optimized. In the optimized process, the curing temperature and pressure were kept unchanged, and the curing time was shortened by 7 min. The experimental testing results showed that the physical properties of the tire rubber compounds and adhesion strength between belt layers were similar to those by using old process, but the tire durability was improved, the vulcanization process showed good stability, and the production eff iciency was signif icantly improved.