A series of SBA-15 supported bimetallic Rh–Ni catalysts with different weight ratio of Rh/Ni in the range of 0–0.04 were prepared for carbon dioxide reforming of methane. The doping effect of Rh on catalytic activity as well as carbon accumulation and removal over the catalysts was studied. The characterization results indicated that the addition of a small amount of Rh promoted the reducibility of Ni particles and decreased the Ni particle size. During the dry reforming reaction, the carbon deposition was originated from CH4 decomposition and CO disproportionation. The Rh–Ni catalyst with small metallic particle size inhibited the carbon formation and exhibited high efficiency in the removal of coke. In comparison with bare Ni-based catalyst, the Rh–Ni bimetallic catalysts showed high activity and stability in the dry reforming of methane.
A series of SBA-15 supported bimetallic Rh–Ni catalysts with different weight ratio of Rh/Ni in the range of 0–0.04 were prepared for carbon dioxide reforming of methane. The doping effect of Rh on catalytic activity as well as carbon accumulation and removal over the catalysts was studied. The characterization results indicated that the addition of a small amount of Rh promoted the reducibility of Ni particles and decreased the Ni particle size. During the dry reforming reaction, the carbon deposition was originated from CH4 decomposition and CO disproportionation. The Rh–Ni catalyst with small metallic particle size inhibited the carbon formation and exhibited high efficiency in the removal of coke. In comparison with bare Ni-based catalyst, the Rh–Ni bimetallic catalysts showed high activity and stability in the dry reforming of methane.
基金
supported by the National Natural Science Foundation of China(21173050,21371035)