摘要
Highly efficient Sr2Si5N8：Eu^2＋red emitting phosphor was successfully synthesized by a cost-effective direct silicon nitrida-tion and gas-reduction method. The effects of synthesis parameters, including reaction temperature, heating rate and gas species, on the crystal structure and photoluminescence of the prepared phosphors were studied. Single-phase Sr2Si5N8：Eu^2＋phosphor was ob-tained at 1500℃ with a heating rate of 300℃/h under NH3-1 vol.%CH4 atmosphere using starting silicon and oxide powders. Silicon powder and high heating rate favored the achievement of the pure Sr2Si5N8 phase. Under near-UV to blue light excitation, the obtained Sr2Si5N8：Eu2＋phosphor showed a board red emission band centered at about 625 nm, which agreed well with the phosphors prepared by the conventional solid-state reaction. The possible reaction mechanism was also proposed based on the experimental observations.
Highly efficient Sr2Si5N8：Eu^2＋red emitting phosphor was successfully synthesized by a cost-effective direct silicon nitrida-tion and gas-reduction method. The effects of synthesis parameters, including reaction temperature, heating rate and gas species, on the crystal structure and photoluminescence of the prepared phosphors were studied. Single-phase Sr2Si5N8：Eu^2＋phosphor was ob-tained at 1500℃ with a heating rate of 300℃/h under NH3-1 vol.%CH4 atmosphere using starting silicon and oxide powders. Silicon powder and high heating rate favored the achievement of the pure Sr2Si5N8 phase. Under near-UV to blue light excitation, the obtained Sr2Si5N8：Eu2＋phosphor showed a board red emission band centered at about 625 nm, which agreed well with the phosphors prepared by the conventional solid-state reaction. The possible reaction mechanism was also proposed based on the experimental observations.
基金
supported by National Natural Science Foundation of China(51072191
11179037)
University of Science and Technolgy of China-National Synchrotron Radiation Laboratory(USTC-NSRL)joint funds(KY2060140005)
Anhui Provincial Natural Science Foundation(11040606M11)
Anhui Provincial Education Department(KJ2012A289)