摘要
采用粉末注射成形方法制备了具有高导热性能的AlN陶瓷导热材料 ,研究了烧结温度对注射成形AlN陶瓷致密化的影响 ;研究了添加不同质量分数Y2 O3对注射成形AlN陶瓷的晶界第二相、热导率和显微结构的影响 .结果表明 :在本实验研究条件下 ,当烧结温度在 185 0℃时 ,AlN的相对密度已经能够达到 99.5 % ;Y2 O3的添加量对AlN的晶界第二相的影响和传统AlN制备工艺中有较大的不同 ,在Y2 O3质量分数为 3 %时就有多余的Y2 O3成为晶界相 ,这主要是注射成形工艺中会引入大量的残碳造成的 .注射成形AlN陶瓷工艺中氧离子是否扩散进入晶格中对AlN陶瓷的热性能有一定影响 .当Y2 O3质量分数为 5 %时 ,AlN中的晶界第二相主要为YN和Y2 O3,样品具有最高的热导率167.5W /(m·K) .
Aluminum nitride with high thermal conductivity was produced by powder injection molding. The influence of sintering temperature on densification of AlN body and the effect of Y 2O 3 on the second phase, thermal conductivity and microstructure in powder injection molding (PIM) AlN are discussed in some detail. The results show that AlN reaches 99.5% density under 1 850 ℃ and the influence of Y 2O 3 on the AlN second phase in PIM is different from that of the traditional preparation method. Residual Y 2O 3 second phase appeared when Y 2O 3 content reaches 3% due to the residual carbon generated from the PIM process. When Y 2O 3 content reaches 5%, AlN has the highest thermal conductivity of 167.5 W/(m·K) and the second phases are YN and Y 2O 3.
出处
《硅酸盐学报》
EI
CAS
CSCD
北大核心
2002年第3期289-293,共5页
Journal of The Chinese Ceramic Society
基金
国家"8 63"计划 (715 -0 90 -0 90 )
国家"973"计划(G2 0 0 0 0 672 0 3 )资助项目