摘要
将恒粘度NRVS65用于胎肩胶及缓冲胶 ,与 1#烟胶片进行对比及车间大料替代试验。结果表明 ,VS65的门尼粘度与塑炼后的 1#烟胶片相当 ,加工性能良好 ,可满足现生产工艺要求 ;用VS65等量替代 1#烟胶片 ,对配方适当调整 ,硫化胶的拉伸强度和扯断伸长率较好 。
A comparative test between CV NR --VS65 and 1 # smoked sheet was made in production shoulder and cushion compounds.The results showed that the Mooney viscosity of VS65 was similar to that of masticated 1 # smoked sheet and it could be well processed with the present processing technology;and the better tensile strength and elongation at break of vulcanizate,and the optimum endurance of finished product were obtained by using VS65 instead of 1 # smoked sheet in the same weight if the formula was properly adjusted.
出处
《轮胎工业》
CAS
2002年第6期345-347,共3页
Tire Industry