利用红外吸收光谱和喇曼散射光谱考察了PbO Bi2 O3 B2 O3,PbO Bi2 O3 B2 O3 SiO2 及PbO Bi2 O3 P2 O5系统中B3+,Si4+,P5+离子的配位状态 ,比较了不同玻璃形成体氧化物在重金属氧化物玻璃形成中的作用 .研究结果表明 :在上述各系统重金属氧化物玻璃中 ,B3+,Si4+,P5+分别以孤立的 [BO3]三角体、[SiO4]四面体及不带PO双键的[PO4]四面体形式存在 ;重金属氧化物玻璃的形成主要取决于 [BO3]三角体、[SiO4]和 [PO4]四面体的含量 ,这些氧多面体的作用是对Pb2 +,Bi3+,O2 -的积聚起阻隔作用 ,使之难以排列成晶格结构 。
The coordination status of B 3+ , Si 4+ and P 5+ ions in PbO Bi 2O 3 B 2O 3, PbO Bi 2O 3 B 2O 3 SiO 2 and PbO Bi 2O 3 P 2O 5 system is investigated by using the IR absorption spectra and the Raman spectra, and the effects of different glass network forming oxides on the forming of HMO glasses are compared. The results show that, B 3+ , Si 4+ , P 5+ ions exist in these HMO glasses in the isolated triangles, the isolated tetrahedron and the isolated tetrahedron without PO bond, respectively; the forming of HMO glasses depends upon the content of , or groups, which set back the gathering of Pb 2+ , Bi 3+ , O 2- ions in the melt of HMO glass and result in the forming of the glass amorphous structure.
出处
《中南工业大学学报》
CSCD
北大核心
2001年第4期398-401,共4页
Journal of Central South University of Technology(Natural Science)
基金
国家自然科学基金资助项目 ( 5 9672 0 0 8)
关键词
玻璃
重金属氧化物
网络形成体
glass
triangle
tetrahedron
tetrahedron
heavy-metal oxide