摘要
探索性研究了影响双相纳米晶Nd4 .5Fe76.5-xGaxCo1.0 B18粘结磁体剩磁的快淬工艺条件 ,并给出了一些有意义的结果 。
In the article, technological condition of Dual phase nanocrystalline Nd 4.5 Fe 76.5- x Ga x Co 1.0 B 18 remanence of bonded magnets was explored, and the more solid base was established by this significative result for the problem of broad interest at home and abroad.
出处
《长沙交通学院学报》
2001年第2期13-15,共3页
Journal of Changsha Communications University
关键词
双相纳米晶永磁材料
晶化
制备工艺
剩磁
dual phase nanocrystalline composite magnets
anneal
preparation technology
remanence