By using instrumental micro-indentation technique, the microhardness and Young＇s modulus of SiC particles reinforced aluminum matrix composites were investigated with micro- compression-tester （MCT）. The micro-indentation experiments were performed with different max- imum loads, and with three loading speeds of 2.231, 4.462 and 19.368 mN/s respectively. During the investigation, matrix, particle and interface were tested by micro-indentation experiments. The results exhibit that the variations of Young＇s modulus and microhardness at particle, matrix and interface were highly dependent on the loading conditions （maximum load and loading speed） and the locations of indentation. Micro-indentation hardness experiments of matrix show the indentation size effects, i.e. the indentation hardness decreased with the indentation depth increas- ing. During the analysis, the effect of loading conditions on Young＇s modulus and microhardness were explained. Besides, the elastic-plastic properties of matrix were analyzed. The validity of cal- culated results was identified by finite element simulation. And the simulation results had been pre- liminarily analyzed from statistical aspect.
By using instrumental micro-indentation technique, the microhardness and Young＇s modulus of SiC particles reinforced aluminum matrix composites were investigated with micro- compression-tester （MCT）. The micro-indentation experiments were performed with different max- imum loads, and with three loading speeds of 2.231, 4.462 and 19.368 mN/s respectively. During the investigation, matrix, particle and interface were tested by micro-indentation experiments. The results exhibit that the variations of Young＇s modulus and microhardness at particle, matrix and interface were highly dependent on the loading conditions （maximum load and loading speed） and the locations of indentation. Micro-indentation hardness experiments of matrix show the indentation size effects, i.e. the indentation hardness decreased with the indentation depth increas- ing. During the analysis, the effect of loading conditions on Young＇s modulus and microhardness were explained. Besides, the elastic-plastic properties of matrix were analyzed. The validity of cal- culated results was identified by finite element simulation. And the simulation results had been pre- liminarily analyzed from statistical aspect.
基金
the support received from the National Natural Science Foundation of China (No. 51275414)
the Aeronautical Science Foundation of China (No. 2011ZE53059)