摘要
以铝阳极氧化形成有序的多孔氧化铝为模板，利用交流电在模板孔洞中沉积金属 Ag得到纳米 Ag粒子 /Al2O3组装体系，透射电镜观察证实在氧化铝模板中有金属纳米 Ag粒子存在 .分析了交流电能在孔洞中沉积金属的原因是由于 Al/Al2O3界面的整流特性，测量了 Al/Al2O3界面的 I－ U关系曲线 .
Nano-Ag/Al2O3 assemblies were prepared by alternating current (AC) electrochemical deposition of Ag in the ordered pores of alumina membranes. TEM spectra show that Ag nanoparticles were deposited in porous alumina. The reason that metal was deposited in porous alumina by AC was attributed to rectifying properties of Al/Al2O3 interface. I - U curve of Al/Al2O3 interface was measured.