在新设计制造的HLX-1型树脂固化仪上对T_(31)-环氧树脂E51进行了最佳配方和最佳条件的选择。T_(31)含量为20phr的环氧树脂体系,最佳固化温度为333K,固化反应活化能E=52.7KJ/mol。用非平衡态涨落理论也成功地预估了T_(31)-环氧树脂体系的固化行为。
New HLX-1 Resin Curometer has been designed and built, by which the curing conditions of T31-epoxy resin E51 system was optimized. The optimum curing temperature for E51 epoxy resin-T_(31)curing agent system is 333K, when the content of curing agent is 20 phr. The estimated apparent activation energy of cure reaction is 52.7 KJ/mol. The nonequilibrium thermodynamic fluctuation theory was used to predict the cure behavior of T31-epoxy E51 system.