Material Characterization of Ni Base Alloy for Very High Temperature Reactor 被引量:4

Material Characterization of Ni Base Alloy for Very High Temperature Reactor
原文传递
导出
摘要 The generation of highly efficient electricity and the production of massive hydrogen are possible using a very high temperature reactor (VHTR) among generation IV nuclear power plants. The structural material for an intermediate heat exchanger (IHX) among numerous components should be endurable at high temperature of up to 950 °C during long-term operation. Impurities inevitably introduced in helium as a coolant facilitate the material degradation by corrosion at high temperature. In the present work, the surface reactions available under controlled impure helium at 950 °C were investigated based on the thermodynamics and the corrosion tests were performed in a temperature range of 850-950 °C during 10-250 h for commercial Alloy 617 as a candidate material for an IHX. Moreover, the mechanical property and microstructure for nickel-based alloys fabricated in laboratory were evaluated as a function of the processing parameters such as hot rolling and heat treatment conditions. From the reaction rate constant obtained from an impure helium control system for a material evaluation, it was predicted that the outer oxide layer thickness, internal oxide depth, and carbide- depleted zone depth reach about 116, 600 and 1000 μm, respectively when Alloy 617 is exposed to an impure helium environment at 950 ~C for 20 years. For Ni-Cr-Co-Mo alloy, subsequent annealing and a combination of cold working and subsequent annealing following solution annealing caused increases in the grain boundary carbide coverage and size. The angular distribution of the grain boundary as well as the carbide distribution was also changed leading to a consequent improvement of the mechanical property at 950 °C in air. The generation of highly efficient electricity and the production of massive hydrogen are possible using a very high temperature reactor (VHTR) among generation IV nuclear power plants. The structural material for an intermediate heat exchanger (IHX) among numerous components should be endurable at high temperature of up to 950 °C during long-term operation. Impurities inevitably introduced in helium as a coolant facilitate the material degradation by corrosion at high temperature. In the present work, the surface reactions available under controlled impure helium at 950 °C were investigated based on the thermodynamics and the corrosion tests were performed in a temperature range of 850-950 °C during 10-250 h for commercial Alloy 617 as a candidate material for an IHX. Moreover, the mechanical property and microstructure for nickel-based alloys fabricated in laboratory were evaluated as a function of the processing parameters such as hot rolling and heat treatment conditions. From the reaction rate constant obtained from an impure helium control system for a material evaluation, it was predicted that the outer oxide layer thickness, internal oxide depth, and carbide- depleted zone depth reach about 116, 600 and 1000 μm, respectively when Alloy 617 is exposed to an impure helium environment at 950 ~C for 20 years. For Ni-Cr-Co-Mo alloy, subsequent annealing and a combination of cold working and subsequent annealing following solution annealing caused increases in the grain boundary carbide coverage and size. The angular distribution of the grain boundary as well as the carbide distribution was also changed leading to a consequent improvement of the mechanical property at 950 °C in air.
出处 《Journal of Materials Science & Technology》 SCIE EI CAS CSCD 2013年第12期1184-1190,共7页 材料科学技术(英文版)
基金 supported by the Ministry of Education,Science and Technology (MEST) of Korea
关键词 Nickel base alloy Intermediate heat exchanger High temperature reactor CORROSION Mechanical property Nickel base alloy Intermediate heat exchanger High temperature reactor Corrosion Mechanical property
  • 相关文献

参考文献12

  • 1Li Jiang,Rui Hu,Hongchao Kou,Jinshan Li,Guanghai Bai,Hengzhi Fu.The effect of M 23 C 6 carbides on the formation of grain boundary serrations in a wrought Ni-based superalloy[J].Materials Science & Engineering A.2011
  • 2S. Schlegel,S. Hopkins,E. Young,J. Cole,T. Lillo,M. Frary.Precipitate Redistribution during Creep of Alloy 617[J].Metallurgical and Materials Transactions A.2009(12)
  • 3Tan, L.,Sridharan, K.,Allen, T.R.,Nanstad, R.K.,McClintock, D.A.Microstructure tailoring for property improvements by grain boundary engineering[].Journal of Nuclear Materials.2008
  • 4Reed R C.The Superalloys Fundamentals and Applications[].Journal of Women s Health.2006
  • 5H.J. Christ,U. Kunecke,K. Meyer,H.G. Sockel. Materials Science and Engineering . 1987
  • 6Brenner,K. G. E.,Graham,L. W. Nuclear Technology . 1984
  • 7Donachie, M.J,Donachie, S.J.Superalloys A technical Guide[].ASM International.2002
  • 8C.Cabet,F.Rouillard. J.Nucl.Mater . 2009
  • 9M.R.Quadakkers. Werkst.Korros . 1984
  • 10C.Cabet,B.Duprey. Proceeding to HTR 2010 . 2010

同被引文献17

引证文献4

二级引证文献9

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部