5083铝合金搅拌摩擦焊焊核区非均匀性组织分析 被引量:1

Research on Heterogeneity Microstructure of 5083 Aluminum in Nugget Zones after Friction Stir Welding
在线阅读 下载PDF
导出
摘要 利用小型搅拌摩擦焊机焊接5083铝合金板材,借助电子背散射衍射技术和取向成像分析软件对焊缝焊核区的焊核前进侧、焊核中心区和焊核后退侧的晶粒形貌和取向差角度进行了对比性研究.结果表明:经过搅拌摩擦焊接后,焊核区发生动态再结晶,晶粒由原始带状转变为等轴状,其大角度晶界含量相比于母材有明显增加,但不同部位的晶粒尺寸和大角度晶界比例均不同,焊核前进侧、焊核中心区和焊核后退侧的平均晶粒尺寸分别为17.0、15.8和13.5μm,大角度晶界比例分别为76.4%、68.8%和73.2%. The 5083-H321 aluminum magnesium alloy plates were welded on a minitype friction stir weld- ing machine. The mierostructure of friction stir welding (FSW) in each nugget zone was studied via the grain morphology and misorientation distribution of nugget advancing side, nugget median zone and nug- get retreating side. The results show that there are small equiaxial grains into which lath-shaped grains turn in nugget zones after friction stir welding. However, there are differences in the grain size between the nugget advancing side, nugget median zone and nugget retreating side, and the average grain sides are 17, 15.8 and 13.5 μm, respectively. Compared with the base metal, the high angle grain bounda- ries (HAGB) fraction in nugget zones increase. Meanwhile the content is also different in the three zones, and they are 76. 4% , 68.8% and 73.2% , respectively.
出处 《广东工业大学学报》 CAS 2013年第3期118-121,共4页 Journal of Guangdong University of Technology
基金 广东省重大科技专项资助项目(2008A090300004) 广东省教育厅211工程学科建设资助项目(412110903)
关键词 搅拌摩擦焊 焊核前进侧 焊核中心区 焊核后退侧 微观组织 friction stir welding nugget advancing side nugget median zone nugget retreating side microstructure
  • 相关文献

参考文献21

  • 1Mishra R S. Preface to the Viewpoint Set on friction stir processing[ J ]. Scripta Materialia, 2008,58 ( 5 ) : 325- 326.
  • 2史耀武,唐伟.搅拌摩擦焊的原理与应用[J].电焊机,2000,30(1):6-9. 被引量:48
  • 3Nandan R, DebRoy T, H. K. D. H. Bhadeshia. Recent ad- vances in friction-stir welding-Process, weldment structure and properties [ J ]. Progress in Materials Science, 2008, 53(6) : 980-1023.
  • 4Gemme F, Verreman Y, Dubourg L, et al. Effect of weld- ing parameters on microstructure and mechanical properties of AA7075-T6 friction stir welded joints [ J ]. Fracture of Engineering Materials and Structures, 2011,34 (11 ) : 877- 886.
  • 5Dehghani K, Chabok A. Dependence of zener parameter on the nanograins formed during friction stir processing of in- terstitial free steels[J]. Materials Science and Engineering A, 2011,528(13-14): 4325-4330.
  • 6Mishra R S, Ma Z Y. Friction stir welding and processing [J]. Materials Science and Engineering R, 2005,50 (1- 2) : 1-78.
  • 7姜玉恒,刘金合,周卫涛.7050铝合金搅拌摩擦焊接头微观组织及力学性能分析[J].电焊机,2012,42(7):86-89. 被引量:6
  • 8董鹏,孙大千,李洪梅,宫文彪,刘杰.6005A-T6铝合金搅拌摩擦焊接头组织与力学性能特征[J].材料工程,2012,40(4):27-31. 被引量:30
  • 9Simar A, Brechet Y, de Meester B, et al. Microstructure, local and global mechanical properties of friction stir welds in aluminium alloy 6005A-T6 [ J ]. Materials Science and Engineering A, 2008,486(1-2) : 85-95.
  • 10唐明君,吉泽升,吕新宇.5×××系铝合金的研究进展[J].轻合金加工技术,2004,32(7):1-7. 被引量:57

二级参考文献102

  • 1杨长贺,孙军,高洪吾.旋转喷头法对铝液的高效除氢作用[J].特种铸造及有色合金,1995,15(3):6-7. 被引量:6
  • 2柴鹏,栾国红,郭德伦,李菊.FSW接头残余应力分布及控制技术[J].焊接学报,2005,26(11):79-82. 被引量:22
  • 3赵衍华,林三宝,申家杰,吴林.2014铝合金搅拌摩擦焊接头的微观组织及力学性能[J].航空材料学报,2006,26(1):67-70. 被引量:23
  • 4Thomas W M, Nicholas E D, Needham J C, Murch M G, Templesmith P, Dawes C J. Gr Br Pat Appl No. 9 125 978.8, 1991.
  • 5Mishra R S, Ma Z Y. Mater Sci Eng, 2005; R50:1.
  • 6Tang W, Guo X, McClure J C, Murr L E. J Mater Process Manuf Sci, 1998; 7(2): 163.
  • 7Staron P, Kocak M. In: David S A, Debroy T, Lippold J C, Smartt H B, Vitek J M eds., Proc 6th Int Conf on Trends in Welding Research, Pine Mountain: ASM International,2003:216.
  • 8Song M, Kovacevic R. J Eng Manuf, 2003; 217(1): 73.
  • 9Colegrove P A, Shercliff H R. Sci Technol Weld Join, 2003; 8:360.
  • 10Chao Y J, Qi X, Tang W. Trans ASME, 2003; 125:138.

共引文献175

同被引文献3

引证文献1

二级引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部