采用颗粒堆积法,以石英砂为骨料,甲基纤维素为黏结剂干压成型后,在1300℃保温1h烧结制备得到SiO2多孔陶瓷样品。通过对样品吸波性能的测试,发现样品的吸波带较宽达到9GHz,反射率约-3dB。经过浸渍氧化石墨烯后,样品的吸波性能发生较大改变。在氧化石墨烯质量分数为0.004%时,由于氧化石墨烯的涡流损耗,样品的吸波性能较纯SiO2多孔陶瓷样品的吸波性能提高75%,反射率达到-5dB。过量的氧化石墨烯使多孔陶瓷样品呈现出对电磁波的全反射。
A particle packing method was developed to prepare porous silica ceramics aggregated by sintering silica powder with methyl cellulose as binding agent at 1300℃ for 1 h.The result of electromagnetic wave absorption showed obvious electromagnetic wave absorption properties with a bandwidth of 9 GHz and-3 dB reflectivity.The electromagnetic wave absorption properties changed after graphene oxide（GO）layers were incorporated into the samples.When the mass fraction of graphene oxide impregnated samples was 0.004%,an increase of 75% in absorption was observed with the greatest reflectivity of-5 dB.The eddy current damping caused by these GO layers was responsible for the enhanced absorption efficiency.While excess GO made the porous sample to be a reflector for incident waves.
出处
《化工学报》
EI
CAS
CSCD
北大核心
2013年第7期2696-2700,共5页
CIESC Journal
关键词
石英砂
多孔陶瓷
吸波性能
石墨烯
silica
porous ceramic
electromagnetic wave absorption properties
graphene