摘要
Gold nanoparticles （NPs） of various shapes were synthesized by a one-step method at ambient temperature in the presence of NaCl. 2-mercaptosuccinic acid （MSA） was used as both reducing agent and stabilizing agent. The shapes of gold NPs were controllable by simply tuning S/Au ratio （S is from MSA molecule, and S/Au ratio is controlled by tuning the volume of added MSA solution）, and triangle, polygonal and spherical nanoparticles were obtained. This result suggested a new way to consider the effects of MSA on the growth of nanoparticles, which showed that MSA is a strong capping agent and facilitates more uniform growth of nanoparticles in every dimension. And other important factors on nanoparticles growth including NaCl and temperature were discussed. Furthermore, a typical probe molecule, 4-aminothiophenol （4-ATP） was used to test the surface-enhanced Raman scattering （SERS） activity of these gold NPs and the results indicated good Raman activity on these substrates. And the enhancement factor （EF） at 1078 cm^- 1 （a1） was estimated to be as large as 6.3 × 10^4 and 5.5 × 10^4 for triangular plates and truncated particles, respectively.
Gold nanoparticles （NPs） of various shapes were synthesized by a one-step method at ambient temperature in the presence of NaCl. 2-mercaptosuccinic acid （MSA） was used as both reducing agent and stabilizing agent. The shapes of gold NPs were controllable by simply tuning S/Au ratio （S is from MSA molecule, and S/Au ratio is controlled by tuning the volume of added MSA solution）, and triangle, polygonal and spherical nanoparticles were obtained. This result suggested a new way to consider the effects of MSA on the growth of nanoparticles, which showed that MSA is a strong capping agent and facilitates more uniform growth of nanoparticles in every dimension. And other important factors on nanoparticles growth including NaCl and temperature were discussed. Furthermore, a typical probe molecule, 4-aminothiophenol （4-ATP） was used to test the surface-enhanced Raman scattering （SERS） activity of these gold NPs and the results indicated good Raman activity on these substrates. And the enhancement factor （EF） at 1078 cm^- 1 （a1） was estimated to be as large as 6.3 × 10^4 and 5.5 × 10^4 for triangular plates and truncated particles, respectively.
基金
supported by the National Natural Science Foundation of China under Grant No.21101146