Influences of different superplasticizers （ STP. KSJSTO and LMS-P） on rheological behavior of low-cement castables and the mechanisms were analyzed. The shear stress and viscosity under different shear rates of matrix slurry were determined using a NXS-I IA rotary viscometer. Effects of different admixtures on the rheological properties of slurry was analyzed theoretically. Sodium tripolyphosphate and poly＇carboxylate superplasticizers KS-JSTO and LMS-P） can improve the fluidity and initial setting time. With STP. the slurry is plastic flow. With KS-JS70 or LMS-P increasing, the slurrv changes from plastic.flow, pseudoplastic flow to dilatant flow successively. Th, e optimum dosages of STP. KS-JSTO and LMS-P are 0. 15%. 0. 25% and 0. 40%, respectively. KS-JS70 and LMS-P can significantly reduce the slurry viscosity and shear stress to improve the workability of construction. Both shear stress and viscosity shall be taken into account for on-site construction.
Influences of different superplasticizers （ STP. KSJSTO and LMS-P） on rheological behavior of low-cement castables and the mechanisms were analyzed. The shear stress and viscosity under different shear rates of matrix slurry were determined using a NXS-I IA rotary viscometer. Effects of different admixtures on the rheological properties of slurry was analyzed theoretically. Sodium tripolyphosphate and poly＇carboxylate superplasticizers KS-JSTO and LMS-P） can improve the fluidity and initial setting time. With STP. the slurry is plastic flow. With KS-JS70 or LMS-P increasing, the slurrv changes from plastic.flow, pseudoplastic flow to dilatant flow successively. Th, e optimum dosages of STP. KS-JSTO and LMS-P are 0. 15%. 0. 25% and 0. 40%, respectively. KS-JS70 and LMS-P can significantly reduce the slurry viscosity and shear stress to improve the workability of construction. Both shear stress and viscosity shall be taken into account for on-site construction.