摘要
用Gleeble-3500热力模拟试验机对铸态M2高速钢进行1000～1150℃及0.01～1.0 s-1的热压缩变形,获得了铸态M2高速钢的流变曲线,分析了变形后的显微组织特性。结果表明,铸态M2高速钢的流变应力和峰值应变均随变形温度的降低和应变速率的提高而增大,其热变形激活能为550.16 kJ/mol,同时得到了其热变形方程,建议其在1050～1150℃和0.01～1.0 s-1的工艺条件下进行热加工。
The hot compression deformation behavior of as-cast AISI M2 high-speed steel was investigated on a Gleeble-3500 simulator at 1000-1150 ℃ and strain rate of 0. 01-1.0 s^-1. The corresponding flow curves were obtained and hot deformation microstructure was observed. The results show that the flow stress and peak strain increase with increasing strain rate and decreasing deformation temperature. The hot deformation activation energy Q of the steel is about 550.16 kJ/mol, and then the hot deformation equation is obtained. The suggested processing condition is at 1050-1150 ℃ and strain rate range of 0. 01-1.0 s -~