A modified polyacrylamide gel route is applied to synthesize SnO2 nanoparticles. High-quality SnO2 nanoparticles with a uniform size are prepared using different chelating agents. The average particle size of the samples is found to depend on the choice of the chelating agent. The photoluminescence spectrum detected at λex = 230 nm shows a new peak located at 740 nm due to the surface defect level distributed at the nanoparticle boundaries.
A modified polyacrylamide gel route is applied to synthesize SnO2 nanoparticles. High-quality SnO2 nanoparticles with a uniform size are prepared using different chelating agents. The average particle size of the samples is found to depend on the choice of the chelating agent. The photoluminescence spectrum detected at λex = 230 nm shows a new peak located at 740 nm due to the surface defect level distributed at the nanoparticle boundaries.
基金
Project supported by the Joint Fund of the National Natural Science Foundation of China and the China Academy of Engineering Physics (Grant Nos. 11076008 and 61178018)
the Ph.D. Programs Foundation of Ministry of Education of China (Grant No. 20110185110007)